Grade 300 Maraging Steel vs. C67000 Bronze
Grade 300 maraging steel belongs to the iron alloys classification, while C67000 bronze belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 300 maraging steel and the bottom bar is C67000 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 6.5 to 18 | |
| 5.6 to 11 |
| Poisson's Ratio | 0.3 | |
| 0.31 |
| Shear Modulus, GPa | 75 | |
| 42 |
| Shear Strength, MPa | 640 to 1190 | |
| 390 to 510 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 2030 | |
| 660 to 880 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1990 | |
| 350 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 190 |
| Melting Completion (Liquidus), °C | 1480 | |
| 900 |
| Melting Onset (Solidus), °C | 1430 | |
| 850 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 410 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 23 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 2.9 |
| Embodied Energy, MJ/kg | 68 | |
| 49 |
| Embodied Water, L/kg | 150 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 170 | |
| 43 to 62 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 23 | |
| 20 |
| Strength to Weight: Axial, points | 35 to 68 | |
| 23 to 31 |
| Strength to Weight: Bending, points | 28 to 43 | |
| 21 to 26 |
| Thermal Shock Resistance, points | 31 to 62 | |
| 21 to 29 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.15 | |
| 3.0 to 6.0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Cobalt (Co), % | 8.5 to 9.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 63 to 68 |
| Iron (Fe), % | 65 to 68.4 | |
| 2.0 to 4.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 to 0.1 | |
| 2.5 to 5.0 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 |
| Nickel (Ni), % | 18 to 19 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0.5 to 0.8 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 21.8 to 32.5 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |