Grade 32 Titanium vs. Nickel 333

Grade 32 titanium belongs to the titanium alloys classification, while nickel 333 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is grade 32 titanium and the bottom bar is nickel 333.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
210
Elongation at Break, % 11
34
Fatigue Strength, MPa 390
200
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 40
81
Shear Strength, MPa 460
420
Tensile Strength: Ultimate (UTS), MPa 770
630
Tensile Strength: Yield (Proof), MPa 670
270

Thermal Properties

Latent Heat of Fusion, J/g 410
320
Maximum Temperature: Mechanical, °C 310
1010
Melting Completion (Liquidus), °C 1610
1460
Melting Onset (Solidus), °C 1560
1410
Specific Heat Capacity, J/kg-K 550
450
Thermal Conductivity, W/m-K 7.5
11
Thermal Expansion, µm/m-K 8.2
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.0
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 38
55
Density, g/cm3 4.5
8.5
Embodied Carbon, kg CO2/kg material 32
8.5
Embodied Energy, MJ/kg 530
120
Embodied Water, L/kg 180
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
170
Resilience: Unit (Modulus of Resilience), kJ/m3 2100
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
23
Strength to Weight: Axial, points 47
21
Strength to Weight: Bending, points 41
19
Thermal Diffusivity, mm2/s 3.0
2.9
Thermal Shock Resistance, points 63
16

Alloy Composition

Aluminum (Al), % 4.5 to 5.5
0
Carbon (C), % 0 to 0.080
0 to 0.1
Chromium (Cr), % 0
24 to 27
Cobalt (Co), % 0
2.5 to 4.0
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
9.3 to 24.5
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0.6 to 1.2
2.5 to 4.0
Nickel (Ni), % 0
44 to 48
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.11
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0.060 to 0.14
0 to 1.5
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0.6 to 1.4
0
Titanium (Ti), % 88.1 to 93
0
Tungsten (W), % 0
2.5 to 4.0
Vanadium (V), % 0.6 to 1.4
0
Zirconium (Zr), % 0.6 to 1.4
0
Residuals, % 0 to 0.4
0