Grade 33 Titanium vs. ACI-ASTM CE8MN Steel

Grade 33 titanium belongs to the titanium alloys classification, while ACI-ASTM CE8MN steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is grade 33 titanium and the bottom bar is ACI-ASTM CE8MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 23
29
Fatigue Strength, MPa 250
370
Poisson's Ratio 0.32
0.27
Shear Modulus, GPa 41
80
Tensile Strength: Ultimate (UTS), MPa 390
750
Tensile Strength: Yield (Proof), MPa 350
500

Thermal Properties

Latent Heat of Fusion, J/g 420
300
Maximum Temperature: Mechanical, °C 320
1100
Melting Completion (Liquidus), °C 1660
1440
Melting Onset (Solidus), °C 1610
1400
Specific Heat Capacity, J/kg-K 540
480
Thermal Conductivity, W/m-K 21
16
Thermal Expansion, µm/m-K 8.7
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 6.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 55
21
Density, g/cm3 4.5
7.8
Embodied Carbon, kg CO2/kg material 33
4.2
Embodied Energy, MJ/kg 530
58
Embodied Water, L/kg 200
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 86
190
Resilience: Unit (Modulus of Resilience), kJ/m3 590
620
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 35
25
Strength to Weight: Axial, points 24
27
Strength to Weight: Bending, points 26
23
Thermal Diffusivity, mm2/s 8.7
4.2
Thermal Shock Resistance, points 30
21

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.080
Chromium (Cr), % 0.1 to 0.2
22.5 to 25.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.3
56 to 66.4
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 4.5
Nickel (Ni), % 0.35 to 0.55
8.0 to 11
Nitrogen (N), % 0 to 0.030
0.1 to 0.3
Oxygen (O), % 0 to 0.25
0
Palladium (Pd), % 0.010 to 0.020
0
Phosphorus (P), % 0
0 to 0.040
Ruthenium (Ru), % 0.020 to 0.040
0
Silicon (Si), % 0
0 to 1.5
Sulfur (S), % 0
0 to 0.040
Titanium (Ti), % 98.1 to 99.52
0
Residuals, % 0 to 0.4
0