Grade 34 Titanium vs. N06210 Nickel

Grade 34 titanium belongs to the titanium alloys classification, while N06210 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade 34 titanium and the bottom bar is N06210 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
220
Elongation at Break, % 20
51
Fatigue Strength, MPa 310
320
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 41
85
Shear Strength, MPa 320
560
Tensile Strength: Ultimate (UTS), MPa 510
780
Tensile Strength: Yield (Proof), MPa 450
350

Thermal Properties

Latent Heat of Fusion, J/g 420
330
Maximum Temperature: Mechanical, °C 320
980
Melting Completion (Liquidus), °C 1660
1570
Melting Onset (Solidus), °C 1610
1510
Specific Heat Capacity, J/kg-K 540
420
Thermal Expansion, µm/m-K 8.7
12

Otherwise Unclassified Properties

Base Metal Price, % relative 55
85
Density, g/cm3 4.5
9.0
Embodied Carbon, kg CO2/kg material 33
17
Embodied Energy, MJ/kg 530
250
Embodied Water, L/kg 200
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
320
Resilience: Unit (Modulus of Resilience), kJ/m3 960
280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
22
Strength to Weight: Axial, points 31
24
Strength to Weight: Bending, points 31
21
Thermal Shock Resistance, points 39
22

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.015
Chromium (Cr), % 0.1 to 0.2
18 to 20
Cobalt (Co), % 0
0 to 1.0
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.3
0 to 1.0
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
18 to 20
Nickel (Ni), % 0.35 to 0.55
54.8 to 62.5
Nitrogen (N), % 0 to 0.050
0
Oxygen (O), % 0 to 0.35
0
Palladium (Pd), % 0.010 to 0.020
0
Phosphorus (P), % 0
0 to 0.020
Ruthenium (Ru), % 0.020 to 0.040
0
Silicon (Si), % 0
0 to 0.080
Sulfur (S), % 0
0 to 0.020
Tantalum (Ta), % 0
1.5 to 2.2
Titanium (Ti), % 98 to 99.52
0
Vanadium (V), % 0
0 to 0.35
Residuals, % 0 to 0.4
0