Grade 350 Maraging Steel vs. 92-silver 8-tin-oxide
Grade 350 maraging steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 5 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is grade 350 maraging steel and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 4.1 to 18 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 98 to 190 | |
| 62 to 110 |
| Shear Strength, MPa | 710 to 1400 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 to 2420 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 830 to 2300 | |
| 120 to 300 |