Grade 350 Maraging Steel vs. C71500 Copper-nickel
Grade 350 maraging steel belongs to the iron alloys classification, while C71500 copper-nickel belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 350 maraging steel and the bottom bar is C71500 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Poisson's Ratio | 0.3 | |
| 0.33 |
| Shear Modulus, GPa | 75 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 to 2420 | |
| 380 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 230 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1240 |
| Melting Onset (Solidus), °C | 1420 | |
| 1170 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 400 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 41 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 5.1 |
| Embodied Energy, MJ/kg | 74 | |
| 74 |
| Embodied Water, L/kg | 160 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 38 to 82 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 29 to 49 | |
| 13 to 18 |
| Thermal Shock Resistance, points | 35 to 74 | |
| 12 to 20 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Cobalt (Co), % | 11.5 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 63.5 to 70.6 |
| Iron (Fe), % | 61.2 to 64.6 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 |
| Nickel (Ni), % | 18 to 19 | |
| 29 to 33 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 1.3 to 1.6 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |