Grade 36 Titanium vs. AISI 316 Stainless Steel
Grade 36 titanium belongs to the titanium alloys classification, while AISI 316 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 36 titanium and the bottom bar is AISI 316 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 11 | |
| 8.0 to 55 |
| Fatigue Strength, MPa | 300 | |
| 210 to 430 |
| Poisson's Ratio | 0.36 | |
| 0.28 |
| Shear Modulus, GPa | 39 | |
| 78 |
| Shear Strength, MPa | 320 | |
| 350 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 530 | |
| 520 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 520 | |
| 230 to 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 590 |
| Melting Completion (Liquidus), °C | 2020 | |
| 1400 |
| Melting Onset (Solidus), °C | 1950 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 470 |
| Thermal Expansion, µm/m-K | 8.1 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.3 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 58 | |
| 3.9 |
| Embodied Energy, MJ/kg | 920 | |
| 53 |
| Embodied Water, L/kg | 130 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 | |
| 85 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1260 | |
| 130 to 1820 |
| Stiffness to Weight: Axial, points | 9.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 23 | |
| 18 to 41 |
| Strength to Weight: Bending, points | 23 | |
| 18 to 31 |
| Thermal Shock Resistance, points | 45 | |
| 11 to 26 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Hydrogen (H), % | 0 to 0.0035 | |
| 0 |
| Iron (Fe), % | 0 to 0.030 | |
| 62 to 72 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 0 | |
| 10 to 14 |
| Niobium (Nb), % | 42 to 47 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 to 0.1 |
| Oxygen (O), % | 0 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 52.3 to 58 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |