Grade 360 Molybdenum vs. Solder Alloy 301

Both grade 360 molybdenum and solder alloy 301 are otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is grade 360 molybdenum and the bottom bar is solder alloy 301.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 310
40
Elongation at Break, % 6.3 to 17
51
Poisson's Ratio 0.31
0.34
Shear Modulus, GPa 120
15
Tensile Strength: Ultimate (UTS), MPa 430 to 620
55
Tensile Strength: Yield (Proof), MPa 270 to 530
49

Thermal Properties

Latent Heat of Fusion, J/g 370
55
Specific Heat Capacity, J/kg-K 250
160
Thermal Expansion, µm/m-K 7.0
14

Otherwise Unclassified Properties

Density, g/cm3 10
8.7
Embodied Carbon, kg CO2/kg material 28
13
Embodied Energy, MJ/kg 330
210

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 37 to 64
27
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 450
30
Stiffness to Weight: Axial, points 17
2.5
Stiffness to Weight: Bending, points 22
13
Strength to Weight: Axial, points 12 to 17
1.8
Strength to Weight: Bending, points 12 to 16
3.7
Thermal Shock Resistance, points 14 to 21
7.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
56.5 to 59
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.030
0
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.010
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Molybdenum (Mo), % 99.9 to 100
0
Nickel (Ni), % 0 to 0.0020
0 to 0.010
Nitrogen (N), % 0 to 0.0020
0
Oxygen (O), % 0 to 0.0015
0
Silicon (Si), % 0 to 0.010
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
41 to 43
Zinc (Zn), % 0
0 to 0.0010