Grade 360 Molybdenum vs. Nickel 200

Grade 360 molybdenum belongs to the otherwise unclassified metals classification, while nickel 200 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 360 molybdenum and the bottom bar is nickel 200.

Grade 360 Molybdenum Nickel Alloy 200 (2.4066, N02200, NA11)

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		180

Elongation at Break, %		6.3 to 17
Elongation at Break, %		23 to 44

Poisson's Ratio		0.31
Poisson's Ratio		0.31

Shear Modulus, GPa		120
Shear Modulus, GPa		70

Tensile Strength: Ultimate (UTS), MPa		430 to 620
Tensile Strength: Ultimate (UTS), MPa		420 to 540

Tensile Strength: Yield (Proof), MPa		270 to 530
Tensile Strength: Yield (Proof), MPa		120 to 370

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		290

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.9

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		11

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		150

Embodied Water, L/kg		360
Embodied Water, L/kg		230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37 to 64
Resilience: Ultimate (Unit Rupture Work), MJ/m³		110 to 150

Resilience: Unit (Modulus of Resilience), kJ/m³		120 to 450
Resilience: Unit (Modulus of Resilience), kJ/m³		42 to 370

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		11

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		21

Strength to Weight: Axial, points		12 to 17
Strength to Weight: Axial, points		13 to 17

Strength to Weight: Bending, points		12 to 16
Strength to Weight: Bending, points		14 to 17

Thermal Shock Resistance, points		14 to 21
Thermal Shock Resistance, points		13 to 16

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0 to 0.15

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 0.010
Iron (Fe), %		0 to 0.4

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.35

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		0

Nickel (Ni), %		0 to 0.0020
Nickel (Ni), %		99 to 100

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0015
Oxygen (O), %		0

Silicon (Si), %		0 to 0.010
Silicon (Si), %		0 to 0.35

Sulfur (S), %		0
Sulfur (S), %		0 to 0.010