Grade 360 Molybdenum vs. N06230 Nickel

Grade 360 molybdenum belongs to the otherwise unclassified metals classification, while N06230 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 360 molybdenum and the bottom bar is N06230 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 310
210
Elongation at Break, % 6.3 to 17
38 to 48
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 120
83
Tensile Strength: Ultimate (UTS), MPa 430 to 620
620 to 840
Tensile Strength: Yield (Proof), MPa 270 to 530
330 to 400

Thermal Properties

Latent Heat of Fusion, J/g 370
310
Specific Heat Capacity, J/kg-K 250
420
Thermal Expansion, µm/m-K 7.0
13

Otherwise Unclassified Properties

Density, g/cm3 10
9.5
Embodied Carbon, kg CO2/kg material 28
11
Embodied Energy, MJ/kg 330
160
Embodied Water, L/kg 360
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 37 to 64
200 to 330
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 450
250 to 380
Stiffness to Weight: Axial, points 17
12
Stiffness to Weight: Bending, points 22
21
Strength to Weight: Axial, points 12 to 17
18 to 25
Strength to Weight: Bending, points 12 to 16
17 to 21
Thermal Shock Resistance, points 14 to 21
17 to 23

Alloy Composition

Aluminum (Al), % 0
0.2 to 0.5
Boron (B), % 0
0 to 0.015
Carbon (C), % 0 to 0.030
0.050 to 0.15
Chromium (Cr), % 0
20 to 24
Cobalt (Co), % 0
0 to 5.0
Iron (Fe), % 0 to 0.010
0 to 3.0
Lanthanum (La), % 0
0.0050 to 0.050
Manganese (Mn), % 0
0.3 to 1.0
Molybdenum (Mo), % 99.9 to 100
1.0 to 3.0
Nickel (Ni), % 0 to 0.0020
47.5 to 65.2
Nitrogen (N), % 0 to 0.0020
0
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.010
0.25 to 0.75
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 0
13 to 15