Grade 360 Molybdenum vs. N07041 Nickel
Grade 360 molybdenum belongs to the otherwise unclassified metals classification, while N07041 nickel belongs to the nickel alloys. There are 14 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 360 molybdenum and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 310 | |
220 |
Elongation at Break, % | 6.3 to 17 | |
14 |
Tensile Strength: Ultimate (UTS), MPa | 430 to 620 | |
1400 |
Tensile Strength: Yield (Proof), MPa | 270 to 530 | |
1050 |
Thermal Properties
Specific Heat Capacity, J/kg-K | 250 | |
450 |
Thermal Expansion, µm/m-K | 7.0 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 10 | |
8.2 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 37 to 64 | |
180 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 450 | |
2510 |
Stiffness to Weight: Axial, points | 17 | |
15 |
Stiffness to Weight: Bending, points | 22 | |
25 |
Strength to Weight: Axial, points | 12 to 17 | |
47 |
Strength to Weight: Bending, points | 12 to 16 | |
34 |
Thermal Shock Resistance, points | 14 to 21 | |
38 |