Grade 361 Molybdenum vs. 85-platinum 15-iridium
Both grade 361 molybdenum and 85-platinum 15-iridium are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 361 molybdenum and the bottom bar is 85-platinum 15-iridium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 220 |
| Elongation at Break, % | 6.3 | |
| 5.5 to 34 |
| Poisson's Ratio | 0.31 | |
| 0.38 |
| Shear Modulus, GPa | 120 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 560 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 110 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 130 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 8.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 22 |
Common Calculations
| Stiffness to Weight: Axial, points | 17 | |
| 5.7 |
| Stiffness to Weight: Bending, points | 22 | |
| 9.3 |
| Strength to Weight: Axial, points | 17 | |
| 7.1 to 9.3 |
| Strength to Weight: Bending, points | 16 | |
| 6.9 to 8.3 |
| Thermal Shock Resistance, points | 21 | |
| 21 to 28 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Iridium (Ir), % | 0 | |
| 14.5 to 15.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 99.9 to 100 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0070 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 84.3 to 85.5 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |