Grade 361 Molybdenum vs. EN 1.4612 Stainless Steel

Grade 361 molybdenum belongs to the otherwise unclassified metals classification, while EN 1.4612 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 361 molybdenum and the bottom bar is EN 1.4612 stainless steel.

Grade 361 Molybdenum EN 1.4612 (X1CrNiMoAlTi12-11-2) Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		6.3
Elongation at Break, %		11

Poisson's Ratio		0.31
Poisson's Ratio		0.28

Shear Modulus, GPa		120
Shear Modulus, GPa		76

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		1690 to 1850

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		1570 to 1730

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		280

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		11

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		3.6

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		50

Embodied Water, L/kg		360
Embodied Water, L/kg		140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		190 to 210

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		60 to 65

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		40 to 43

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		58 to 63

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		1.4 to 1.8

Carbon (C), %		0 to 0.010
Carbon (C), %		0 to 0.015

Chromium (Cr), %		0
Chromium (Cr), %		11 to 12.5

Iron (Fe), %		0 to 0.010
Iron (Fe), %		71.5 to 75.5

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.1

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		1.8 to 2.3

Nickel (Ni), %		0 to 0.0050
Nickel (Ni), %		10.2 to 11.3

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0 to 0.010

Oxygen (O), %		0 to 0.0070
Oxygen (O), %		0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.010

Silicon (Si), %		0 to 0.010
Silicon (Si), %		0 to 0.1

Sulfur (S), %		0
Sulfur (S), %		0 to 0.0050

Titanium (Ti), %		0
Titanium (Ti), %		0.2 to 0.5