Grade 361 Molybdenum vs. Grade CW6M Nickel

Grade 361 molybdenum belongs to the otherwise unclassified metals classification, while grade CW6M nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade 361 molybdenum and the bottom bar is grade CW6M nickel.

Grade 361 Molybdenum Grade CW6M (J30107) Cast Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		220

Elongation at Break, %		6.3
Elongation at Break, %		29

Poisson's Ratio		0.31
Poisson's Ratio		0.29

Shear Modulus, GPa		120
Shear Modulus, GPa		84

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		560

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		310

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		330

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		430

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		13

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		170

Embodied Water, L/kg		360
Embodied Water, L/kg		300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		140

Resilience: Unit (Modulus of Resilience), kJ/m³		450
Resilience: Unit (Modulus of Resilience), kJ/m³		220

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		17

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		16

Alloy Composition

Carbon (C), %		0 to 0.010
Carbon (C), %		0 to 0.070

Chromium (Cr), %		0
Chromium (Cr), %		17 to 20

Iron (Fe), %		0 to 0.010
Iron (Fe), %		0 to 3.0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		17 to 20

Nickel (Ni), %		0 to 0.0050
Nickel (Ni), %		54.9 to 66

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0070
Oxygen (O), %		0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 0.010
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030