Grade 361 Molybdenum vs. Grade N12MV Nickel

Grade 361 molybdenum belongs to the otherwise unclassified metals classification, while grade N12MV nickel belongs to the nickel alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is grade 361 molybdenum and the bottom bar is grade N12MV nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 310
220
Elongation at Break, % 6.3
6.8
Poisson's Ratio 0.31
0.31
Shear Modulus, GPa 120
84
Tensile Strength: Ultimate (UTS), MPa 620
600
Tensile Strength: Yield (Proof), MPa 530
310

Thermal Properties

Latent Heat of Fusion, J/g 370
320
Specific Heat Capacity, J/kg-K 250
390
Thermal Expansion, µm/m-K 7.0
10

Otherwise Unclassified Properties

Density, g/cm3 10
9.2
Embodied Carbon, kg CO2/kg material 28
16
Embodied Energy, MJ/kg 330
200
Embodied Water, L/kg 360
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 37
34
Resilience: Unit (Modulus of Resilience), kJ/m3 450
220
Stiffness to Weight: Axial, points 17
13
Stiffness to Weight: Bending, points 22
22
Strength to Weight: Axial, points 17
18
Strength to Weight: Bending, points 16
17
Thermal Shock Resistance, points 21
19

Alloy Composition

Carbon (C), % 0 to 0.010
0 to 0.12
Chromium (Cr), % 0
0 to 1.0
Iron (Fe), % 0 to 0.010
4.0 to 6.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 99.9 to 100
26 to 30
Nickel (Ni), % 0 to 0.0050
60.2 to 69.8
Nitrogen (N), % 0 to 0.0020
0
Oxygen (O), % 0 to 0.0070
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.010
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
0.2 to 0.6