Grade 361 Molybdenum vs. Solder Alloy 701

Both grade 361 molybdenum and solder alloy 701 are otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 361 molybdenum and the bottom bar is solder alloy 701.

Grade 361 MolybdenumISO Solder Alloy 701 (IEC A37, Sn96.3Ag3.7)
Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 310
51
Elongation at Break, % 6.3
37
Poisson's Ratio 0.31
0.36
Shear Modulus, GPa 120
19
Tensile Strength: Ultimate (UTS), MPa 620
54

Thermal Properties

Latent Heat of Fusion, J/g 370
61
Specific Heat Capacity, J/kg-K 250
220
Thermal Expansion, µm/m-K 7.0
22

Otherwise Unclassified Properties

Density, g/cm3 10
7.4
Embodied Carbon, kg CO2/kg material 28
18
Embodied Energy, MJ/kg 330
300

Common Calculations

Stiffness to Weight: Axial, points 17
3.8
Stiffness to Weight: Bending, points 22
17
Strength to Weight: Axial, points 17
2.0
Strength to Weight: Bending, points 16
4.3
Thermal Shock Resistance, points 21
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.010
0
Copper (Cu), % 0
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.010
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Molybdenum (Mo), % 99.9 to 100
0
Nickel (Ni), % 0 to 0.0050
0 to 0.010
Nitrogen (N), % 0 to 0.0020
0
Oxygen (O), % 0 to 0.0070
0
Silicon (Si), % 0 to 0.010
0
Silver (Ag), % 0
3.5 to 3.9
Tin (Sn), % 0
95.6 to 96.5
Zinc (Zn), % 0
0 to 0.0010