Grade 361 Molybdenum vs. C27200 Brass

Grade 361 molybdenum belongs to the otherwise unclassified metals classification, while C27200 brass belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 361 molybdenum and the bottom bar is C27200 brass.

Grade 361 Molybdenum UNS C27200 Yellow Brass

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		110

Elongation at Break, %		6.3
Elongation at Break, %		10 to 50

Poisson's Ratio		0.31
Poisson's Ratio		0.31

Shear Modulus, GPa		120
Shear Modulus, GPa		40

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		370 to 590

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		150 to 410

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		170

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		20

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.1

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		2.7

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		45

Embodied Water, L/kg		360
Embodied Water, L/kg		320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		30 to 270

Resilience: Unit (Modulus of Resilience), kJ/m³		450
Resilience: Unit (Modulus of Resilience), kJ/m³		110 to 810

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		7.2

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		19

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		13 to 20

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		14 to 19

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		12 to 20

Alloy Composition

Carbon (C), %		0 to 0.010
Carbon (C), %		0

Copper (Cu), %		0
Copper (Cu), %		62 to 65

Iron (Fe), %		0 to 0.010
Iron (Fe), %		0 to 0.070

Lead (Pb), %		0
Lead (Pb), %		0 to 0.070

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		0

Nickel (Ni), %		0 to 0.0050
Nickel (Ni), %		0

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0070
Oxygen (O), %		0

Silicon (Si), %		0 to 0.010
Silicon (Si), %		0

Zinc (Zn), %		0
Zinc (Zn), %		34.6 to 38

Residuals, %		0
Residuals, %		0 to 0.3