Grade 363 Molybdenum vs. Grade 7 Titanium
Grade 363 molybdenum belongs to the otherwise unclassified metals classification, while grade 7 titanium belongs to the titanium alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 363 molybdenum and the bottom bar is grade 7 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 110 |
| Elongation at Break, % | 6.2 to 11 | |
| 24 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 120 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 720 | |
| 420 |
| Tensile Strength: Yield (Proof), MPa | 350 to 620 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 420 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 540 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 9.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 47 |
| Embodied Energy, MJ/kg | 330 | |
| 800 |
| Embodied Water, L/kg | 360 | |
| 470 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 57 | |
| 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 630 | |
| 560 |
| Stiffness to Weight: Axial, points | 17 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 35 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 26 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 28 |
| Thermal Shock Resistance, points | 19 to 24 | |
| 31 |
Alloy Composition
| Carbon (C), % | 0.010 to 0.030 | |
| 0 to 0.080 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 99.3 to 99.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 to 0.0030 | |
| 0 to 0.25 |
| Palladium (Pd), % | 0 | |
| 0.12 to 0.25 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0.4 to 0.55 | |
| 98.7 to 99.88 |
| Zirconium (Zr), % | 0.060 to 0.12 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |