Grade 365 Molybdenum vs. AISI 414 Stainless Steel
Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while AISI 414 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is AISI 414 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 190 |
| Elongation at Break, % | 6.3 | |
| 17 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 120 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 900 to 960 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 700 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 480 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 2.1 |
| Embodied Energy, MJ/kg | 330 | |
| 29 |
| Embodied Water, L/kg | 360 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 37 | |
| 140 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 | |
| 1260 to 1590 |
| Stiffness to Weight: Axial, points | 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 17 | |
| 32 to 34 |
| Strength to Weight: Bending, points | 16 | |
| 27 to 28 |
| Thermal Shock Resistance, points | 21 | |
| 33 to 35 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 11.5 to 13.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 81.8 to 87.3 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 99.9 to 100 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 1.3 to 2.5 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |