Grade 365 Molybdenum vs. EN 1.4401 Stainless Steel
Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while EN 1.4401 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is EN 1.4401 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 200 |
| Elongation at Break, % | 6.3 | |
| 14 to 40 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 120 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 600 to 900 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 230 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 290 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 470 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 3.8 |
| Embodied Energy, MJ/kg | 330 | |
| 52 |
| Embodied Water, L/kg | 360 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 37 | |
| 110 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 | |
| 130 to 800 |
| Stiffness to Weight: Axial, points | 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 17 | |
| 21 to 32 |
| Strength to Weight: Bending, points | 16 | |
| 20 to 26 |
| Thermal Shock Resistance, points | 21 | |
| 13 to 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 to 0.070 |
| Chromium (Cr), % | 0 | |
| 16.5 to 18.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 62.8 to 71.5 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 99.9 to 100 | |
| 2.0 to 2.5 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 10 to 13 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 to 0.1 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |