Grade 365 Molybdenum vs. EN 1.5511 Steel

Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while EN 1.5511 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is EN 1.5511 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 310
190
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 120
72
Tensile Strength: Ultimate (UTS), MPa 620
490 to 580

Thermal Properties

Latent Heat of Fusion, J/g 370
250
Specific Heat Capacity, J/kg-K 250
470
Thermal Expansion, µm/m-K 7.0
13

Otherwise Unclassified Properties

Density, g/cm3 10
7.8
Embodied Carbon, kg CO2/kg material 28
1.4
Embodied Energy, MJ/kg 330
19
Embodied Water, L/kg 360
46

Common Calculations

Stiffness to Weight: Axial, points 17
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 17
17 to 20
Strength to Weight: Bending, points 16
18 to 20
Thermal Shock Resistance, points 21
15 to 17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.010
0.32 to 0.39
Iron (Fe), % 0 to 0.010
98.3 to 99.159
Manganese (Mn), % 0
0.5 to 0.8
Molybdenum (Mo), % 99.9 to 100
0
Nickel (Ni), % 0 to 0.0020
0
Nitrogen (N), % 0 to 0.0020
0
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.010
0 to 0.4
Sulfur (S), % 0
0 to 0.015