Grade 365 Molybdenum vs. Grade 3 Babbitt Metal
Both grade 365 molybdenum and grade 3 Babbitt Metal are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is grade 3 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 56 |
| Poisson's Ratio | 0.31 | |
| 0.35 |
| Shear Modulus, GPa | 120 | |
| 21 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 46 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 79 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 230 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.4 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 12 |
| Embodied Energy, MJ/kg | 330 | |
| 200 |
| Embodied Water, L/kg | 360 | |
| 1210 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 | |
| 19 |
| Stiffness to Weight: Axial, points | 17 | |
| 4.2 |
| Stiffness to Weight: Bending, points | 22 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 7.5 to 8.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.1 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 7.5 to 8.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.080 |
| Lead (Pb), % | 0 | |
| 0 to 0.35 |
| Molybdenum (Mo), % | 99.9 to 100 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 0 | |
| 82.3 to 85 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |