Grade 365 Molybdenum vs. Grade M30H Nickel

Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while grade M30H nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is grade M30H nickel.

Grade 365 Molybdenum Grade M30H (J24030) Cast Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		160

Elongation at Break, %		6.3
Elongation at Break, %		11

Poisson's Ratio		0.31
Poisson's Ratio		0.32

Shear Modulus, GPa		120
Shear Modulus, GPa		61

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		770

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		470

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		320

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.6

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		7.7

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		110

Embodied Water, L/kg		360
Embodied Water, L/kg		250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		75

Resilience: Unit (Modulus of Resilience), kJ/m³		450
Resilience: Unit (Modulus of Resilience), kJ/m³		700

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		10

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		21

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		25

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		22

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		27

Alloy Composition

Carbon (C), %		0 to 0.010
Carbon (C), %		0 to 0.3

Copper (Cu), %		0
Copper (Cu), %		27 to 33

Iron (Fe), %		0 to 0.010
Iron (Fe), %		0 to 3.5

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.5

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		0

Nickel (Ni), %		0 to 0.0020
Nickel (Ni), %		57.9 to 70.3

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0015
Oxygen (O), %		0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.010
Silicon (Si), %		2.7 to 3.7

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030