Grade 365 Molybdenum vs. C95800 Bronze

Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while C95800 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is C95800 bronze.

Grade 365 Molybdenum UNS C95800 Nickel-Aluminum Bronze

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		120

Elongation at Break, %		6.3
Elongation at Break, %		22

Poisson's Ratio		0.31
Poisson's Ratio		0.34

Shear Modulus, GPa		120
Shear Modulus, GPa		44

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		660

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		270

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		230

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		17

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.3

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		3.4

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		55

Embodied Water, L/kg		360
Embodied Water, L/kg		370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		110

Resilience: Unit (Modulus of Resilience), kJ/m³		450
Resilience: Unit (Modulus of Resilience), kJ/m³		310

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		7.9

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		20

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		22

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		20

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		23

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		8.5 to 9.5

Carbon (C), %		0 to 0.010
Carbon (C), %		0

Copper (Cu), %		0
Copper (Cu), %		79 to 83.2

Iron (Fe), %		0 to 0.010
Iron (Fe), %		3.5 to 4.5

Lead (Pb), %		0
Lead (Pb), %		0 to 0.030

Manganese (Mn), %		0
Manganese (Mn), %		0.8 to 1.5

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		0

Nickel (Ni), %		0 to 0.0020
Nickel (Ni), %		4.0 to 5.0

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0015
Oxygen (O), %		0

Silicon (Si), %		0 to 0.010
Silicon (Si), %		0 to 0.1

Residuals, %		0
Residuals, %		0 to 0.5