Grade 365 Molybdenum vs. R30016 Cobalt

Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while R30016 cobalt belongs to the cobalt alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is R30016 cobalt.

Grade 365 Molybdenum UNS R30016 Co-Cr-W Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		220

Elongation at Break, %		6.3
Elongation at Break, %		8.4

Poisson's Ratio		0.31
Poisson's Ratio		0.28

Shear Modulus, GPa		120
Shear Modulus, GPa		85

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		1010

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		580

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		320

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.5

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		7.7

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		110

Embodied Water, L/kg		360
Embodied Water, L/kg		500

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		72

Resilience: Unit (Modulus of Resilience), kJ/m³		450
Resilience: Unit (Modulus of Resilience), kJ/m³		770

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		33

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		26

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		24

Alloy Composition

Carbon (C), %		0 to 0.010
Carbon (C), %		0.9 to 1.4

Chromium (Cr), %		0
Chromium (Cr), %		28 to 32

Cobalt (Co), %		0
Cobalt (Co), %		49.6 to 66.9

Iron (Fe), %		0 to 0.010
Iron (Fe), %		0 to 3.0

Manganese (Mn), %		0
Manganese (Mn), %		0.5 to 2.0

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		0 to 1.5

Nickel (Ni), %		0 to 0.0020
Nickel (Ni), %		0 to 3.0

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0015
Oxygen (O), %		0

Silicon (Si), %		0 to 0.010
Silicon (Si), %		0.2 to 2.0

Tungsten (W), %		0
Tungsten (W), %		3.5 to 5.5