Grade 366 Molybdenum vs. AISI 301L Stainless Steel
Grade 366 molybdenum belongs to the otherwise unclassified metals classification, while AISI 301L stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is grade 366 molybdenum and the bottom bar is AISI 301L stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 300 | |
| 200 |
| Elongation at Break, % | 2.2 | |
| 22 to 50 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 120 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 620 to 1040 |
| Tensile Strength: Yield (Proof), MPa | 470 | |
| 250 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 210 | |
| 480 |
| Thermal Expansion, µm/m-K | 7.6 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 12 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 2.7 |
| Embodied Energy, MJ/kg | 340 | |
| 39 |
| Embodied Water, L/kg | 300 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 | |
| 210 to 300 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 160 to 1580 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 13 | |
| 22 to 37 |
| Strength to Weight: Bending, points | 13 | |
| 21 to 29 |
| Thermal Shock Resistance, points | 18 | |
| 14 to 24 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Iron (Fe), % | 0 to 0.010 | |
| 70.7 to 78 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 66.9 to 73 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 6.0 to 8.0 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 to 0.2 |
| Oxygen (O), % | 0 to 0.0025 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 27 to 33 | |
| 0 |