Grade 366 Molybdenum vs. EN 1.1219 Steel
Grade 366 molybdenum belongs to the otherwise unclassified metals classification, while EN 1.1219 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is grade 366 molybdenum and the bottom bar is EN 1.1219 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 300 | |
| 190 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 120 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 700 to 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 210 | |
| 470 |
| Thermal Expansion, µm/m-K | 7.6 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 12 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 1.4 |
| Embodied Energy, MJ/kg | 340 | |
| 19 |
| Embodied Water, L/kg | 300 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 13 | |
| 25 to 27 |
| Strength to Weight: Bending, points | 13 | |
| 22 to 24 |
| Thermal Shock Resistance, points | 18 | |
| 22 to 25 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.030 | |
| 0.52 to 0.6 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.010 | |
| 98.3 to 99.4 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 66.9 to 73 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0025 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 27 to 33 | |
| 0 |