Grade 366 Molybdenum vs. Nickel 690
Grade 366 molybdenum belongs to the otherwise unclassified metals classification, while nickel 690 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 366 molybdenum and the bottom bar is nickel 690.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 300 | |
| 200 |
| Elongation at Break, % | 2.2 | |
| 3.4 to 34 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 120 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 640 to 990 |
| Tensile Strength: Yield (Proof), MPa | 470 | |
| 250 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 320 |
| Specific Heat Capacity, J/kg-K | 210 | |
| 470 |
| Thermal Expansion, µm/m-K | 7.6 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 12 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 8.2 |
| Embodied Energy, MJ/kg | 340 | |
| 120 |
| Embodied Water, L/kg | 300 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 | |
| 31 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 160 to 1440 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 13 | |
| 21 to 33 |
| Strength to Weight: Bending, points | 13 | |
| 20 to 27 |
| Thermal Shock Resistance, points | 18 | |
| 16 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 27 to 31 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 7.0 to 11 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 66.9 to 73 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 58 to 66 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.0025 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tungsten (W), % | 27 to 33 | |
| 0 |