Grade 7 Babbitt Metal vs. ASTM B477 Au-Ni-Ag
Both grade 7 Babbitt Metal and ASTM B477 Au-Ni-Ag are otherwise unclassified metals. There are 11 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is ASTM B477 Au-Ni-Ag.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 26 | |
| 95 |
| Poisson's Ratio | 0.4 | |
| 0.41 |
| Shear Modulus, GPa | 9.1 | |
| 34 |
Thermal Properties
| Latent Heat of Fusion, J/g | 48 | |
| 80 |
| Melting Completion (Liquidus), °C | 270 | |
| 1010 |
| Melting Onset (Solidus), °C | 240 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 160 |
| Thermal Expansion, µm/m-K | 26 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.4 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 9.6 | |
| 8.9 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 14 to 16 | |
| 0 |
| Arsenic (As), % | 0.3 to 0.6 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Gold (Au), % | 0 | |
| 74.2 to 75.8 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 |
| Lead (Pb), % | 71.9 to 76.4 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 2.6 to 3.4 |
| Silver (Ag), % | 0 | |
| 21.4 to 22.6 |
| Tin (Sn), % | 9.3 to 10.7 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.3 |