Grade 7 Babbitt Metal vs. B535.0 Aluminum
Grade 7 Babbitt Metal belongs to the otherwise unclassified metals classification, while B535.0 aluminum belongs to the aluminum alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is B535.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 23 | |
| 65 |
| Elastic (Young's, Tensile) Modulus, GPa | 26 | |
| 66 |
| Poisson's Ratio | 0.4 | |
| 0.33 |
| Shear Modulus, GPa | 9.1 | |
| 25 |
| Tensile Strength: Yield (Proof), MPa | 25 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 48 | |
| 390 |
| Melting Completion (Liquidus), °C | 270 | |
| 630 |
| Melting Onset (Solidus), °C | 240 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 910 |
| Thermal Expansion, µm/m-K | 26 | |
| 25 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 9.5 |
| Density, g/cm3 | 10 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 9.4 |
| Embodied Energy, MJ/kg | 62 | |
| 160 |
| Embodied Water, L/kg | 880 | |
| 1180 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 12 | |
| 130 |
| Stiffness to Weight: Axial, points | 1.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 9.6 | |
| 51 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 91.7 to 93.4 |
| Antimony (Sb), % | 14 to 16 | |
| 0 |
| Arsenic (As), % | 0.3 to 0.6 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.15 |
| Lead (Pb), % | 71.9 to 76.4 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 6.5 to 7.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 | |
| 0 to 0.15 |
| Tin (Sn), % | 9.3 to 10.7 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.1 to 0.25 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |