Grade 7 Babbitt Metal vs. EN 1.1152 Steel

Grade 7 Babbitt Metal belongs to the otherwise unclassified metals classification, while EN 1.1152 steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is EN 1.1152 steel.

Grade 7 (L53585) Lead-Base Babbitt Metal EN 1.1152 (C20E2C) Non-Alloy Steel

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness		23
Brinell Hardness		120 to 160

Elastic (Young's, Tensile) Modulus, GPa		26
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.4
Poisson's Ratio		0.29

Shear Modulus, GPa		9.1
Shear Modulus, GPa		73

Tensile Strength: Yield (Proof), MPa		25
Tensile Strength: Yield (Proof), MPa		270 to 440

Thermal Properties

Latent Heat of Fusion, J/g		48
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		270
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		150
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		26
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		23
Base Metal Price, % relative		1.8

Density, g/cm³		10
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		4.4
Embodied Carbon, kg CO₂/kg material		1.4

Embodied Energy, MJ/kg		62
Embodied Energy, MJ/kg		18

Embodied Water, L/kg		880
Embodied Water, L/kg		46

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		12
Resilience: Unit (Modulus of Resilience), kJ/m³		200 to 530

Stiffness to Weight: Axial, points		1.4
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		9.6
Stiffness to Weight: Bending, points		24

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		14 to 16
Antimony (Sb), %		0

Arsenic (As), %		0.3 to 0.6
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.1
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0.18 to 0.22

Copper (Cu), %		0 to 0.5
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 0.1
Iron (Fe), %		98.6 to 99.52

Lead (Pb), %		71.9 to 76.4
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0.3 to 0.6

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0
Silicon (Si), %		0 to 0.3

Sulfur (S), %		0
Sulfur (S), %		0 to 0.025

Tin (Sn), %		9.3 to 10.7
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		0