Grade 7 Babbitt Metal vs. EN 1.6526 Steel

Grade 7 Babbitt Metal belongs to the otherwise unclassified metals classification, while EN 1.6526 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is EN 1.6526 steel.

Grade 7 (L53585) Lead-Base Babbitt Metal EN 1.6526 (20NiCrMoS2-2) Steel

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness		23
Brinell Hardness		160 to 190

Elastic (Young's, Tensile) Modulus, GPa		26
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.4
Poisson's Ratio		0.29

Shear Modulus, GPa		9.1
Shear Modulus, GPa		73

Thermal Properties

Latent Heat of Fusion, J/g		48
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		270
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		150
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		26
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		23
Base Metal Price, % relative		2.6

Density, g/cm³		10
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		4.4
Embodied Carbon, kg CO₂/kg material		1.5

Embodied Energy, MJ/kg		62
Embodied Energy, MJ/kg		20

Embodied Water, L/kg		880
Embodied Water, L/kg		50

Common Calculations

Stiffness to Weight: Axial, points		1.4
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		9.6
Stiffness to Weight: Bending, points		24

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		14 to 16
Antimony (Sb), %		0

Arsenic (As), %		0.3 to 0.6
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.1
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0.17 to 0.23

Chromium (Cr), %		0
Chromium (Cr), %		0.35 to 0.7

Copper (Cu), %		0 to 0.5
Copper (Cu), %		0 to 0.25

Iron (Fe), %		0 to 0.1
Iron (Fe), %		96.6 to 98.3

Lead (Pb), %		71.9 to 76.4
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0.65 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.15 to 0.25

Nickel (Ni), %		0
Nickel (Ni), %		0.4 to 0.7

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0
Silicon (Si), %		0 to 0.3

Sulfur (S), %		0
Sulfur (S), %		0.020 to 0.040

Tin (Sn), %		9.3 to 10.7
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		0