Grade 7 Babbitt Metal vs. Grade 200 Maraging Steel
Grade 7 Babbitt Metal belongs to the otherwise unclassified metals classification, while grade 200 maraging steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is grade 200 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 110 | |
| 730 to 1260 |
| Elastic (Young's, Tensile) Modulus, GPa | 26 | |
| 190 |
| Poisson's Ratio | 0.4 | |
| 0.3 |
| Shear Modulus, GPa | 9.1 | |
| 74 |
| Tensile Strength: Yield (Proof), MPa | 25 | |
| 690 to 1490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 48 | |
| 260 |
| Melting Completion (Liquidus), °C | 270 | |
| 1460 |
| Melting Onset (Solidus), °C | 240 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 460 |
| Thermal Expansion, µm/m-K | 26 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 31 |
| Density, g/cm3 | 10 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 4.5 |
| Embodied Energy, MJ/kg | 62 | |
| 59 |
| Embodied Water, L/kg | 880 | |
| 140 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 12 | |
| 1240 to 5740 |
| Stiffness to Weight: Axial, points | 1.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 9.6 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0.050 to 0.15 |
| Antimony (Sb), % | 14 to 16 | |
| 0 |
| Arsenic (As), % | 0.3 to 0.6 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Cobalt (Co), % | 0 | |
| 8.0 to 9.0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 67.8 to 71.8 |
| Lead (Pb), % | 71.9 to 76.4 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 3.5 |
| Nickel (Ni), % | 0 | |
| 17 to 19 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 9.3 to 10.7 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.25 |
| Zinc (Zn), % | 0 to 0.0050 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |