Grade 7 Babbitt Metal vs. Solder Alloy 201
Both grade 7 Babbitt Metal and solder alloy 201 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is solder alloy 201.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 23 | |
13 |
Elastic (Young's, Tensile) Modulus, GPa | 26 | |
50 |
Poisson's Ratio | 0.4 | |
0.35 |
Shear Modulus, GPa | 9.1 | |
19 |
Thermal Properties
Latent Heat of Fusion, J/g | 48 | |
64 |
Melting Completion (Liquidus), °C | 270 | |
240 |
Melting Onset (Solidus), °C | 240 | |
240 |
Specific Heat Capacity, J/kg-K | 150 | |
220 |
Thermal Expansion, µm/m-K | 26 | |
21 |
Otherwise Unclassified Properties
Density, g/cm3 | 10 | |
7.3 |
Embodied Carbon, kg CO2/kg material | 4.4 | |
15 |
Embodied Energy, MJ/kg | 62 | |
250 |
Embodied Water, L/kg | 880 | |
1320 |
Common Calculations
Stiffness to Weight: Axial, points | 1.4 | |
3.8 |
Stiffness to Weight: Bending, points | 9.6 | |
17 |
Alloy Composition
Aluminum (Al), % | 0 to 0.0050 | |
0 to 0.0010 |
Antimony (Sb), % | 14 to 16 | |
4.5 to 5.5 |
Arsenic (As), % | 0.3 to 0.6 | |
0 to 0.030 |
Bismuth (Bi), % | 0 to 0.1 | |
0 to 0.1 |
Cadmium (Cd), % | 0 to 0.050 | |
0 to 0.0020 |
Copper (Cu), % | 0 to 0.5 | |
0 to 0.050 |
Gold (Au), % | 0 | |
0 to 0.050 |
Indium (In), % | 0 | |
0 to 0.1 |
Iron (Fe), % | 0 to 0.1 | |
0 to 0.020 |
Lead (Pb), % | 71.9 to 76.4 | |
0 to 0.070 |
Nickel (Ni), % | 0 | |
0 to 0.010 |
Silver (Ag), % | 0 | |
0 to 0.1 |
Tin (Sn), % | 9.3 to 10.7 | |
94 to 95.5 |
Zinc (Zn), % | 0 to 0.0050 | |
0 to 0.0010 |