Grade 7 Babbitt Metal vs. Nickel 601

Grade 7 Babbitt Metal belongs to the otherwise unclassified metals classification, while nickel 601 belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is nickel 601.

Grade 7 (L53585) Lead-Base Babbitt Metal Nickel Alloy 601 (N06601, NA49)

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		26
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.4
Poisson's Ratio		0.28

Shear Modulus, GPa		9.1
Shear Modulus, GPa		76

Tensile Strength: Yield (Proof), MPa		25
Tensile Strength: Yield (Proof), MPa		290 to 800

Thermal Properties

Latent Heat of Fusion, J/g		48
Latent Heat of Fusion, J/g		320

Melting Completion (Liquidus), °C		270
Melting Completion (Liquidus), °C		1410

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		1360

Specific Heat Capacity, J/kg-K		150
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		26
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		23
Base Metal Price, % relative		49

Density, g/cm³		10
Density, g/cm³		8.3

Embodied Carbon, kg CO₂/kg material		4.4
Embodied Carbon, kg CO₂/kg material		8.0

Embodied Energy, MJ/kg		62
Embodied Energy, MJ/kg		110

Embodied Water, L/kg		880
Embodied Water, L/kg		280

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		12
Resilience: Unit (Modulus of Resilience), kJ/m³		210 to 1630

Stiffness to Weight: Axial, points		1.4
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		9.6
Stiffness to Weight: Bending, points		23

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		1.0 to 1.7

Antimony (Sb), %		14 to 16
Antimony (Sb), %		0

Arsenic (As), %		0.3 to 0.6
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.1
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.1

Chromium (Cr), %		0
Chromium (Cr), %		21 to 25

Copper (Cu), %		0 to 0.5
Copper (Cu), %		0 to 1.0

Iron (Fe), %		0 to 0.1
Iron (Fe), %		7.7 to 20

Lead (Pb), %		71.9 to 76.4
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Nickel (Ni), %		0
Nickel (Ni), %		58 to 63

Silicon (Si), %		0
Silicon (Si), %		0 to 0.5

Sulfur (S), %		0
Sulfur (S), %		0 to 0.015

Tin (Sn), %		9.3 to 10.7
Tin (Sn), %		0

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		0