Grade 7 Babbitt Metal vs. C72900 Copper-nickel

Grade 7 Babbitt Metal belongs to the otherwise unclassified metals classification, while C72900 copper-nickel belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is grade 7 Babbitt Metal and the bottom bar is C72900 copper-nickel.

Grade 7 (L53585) Lead-Base Babbitt Metal UNS C72900 Tin-Bearing Copper-Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		26
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.4
Poisson's Ratio		0.34

Shear Modulus, GPa		9.1
Shear Modulus, GPa		45

Tensile Strength: Yield (Proof), MPa		25
Tensile Strength: Yield (Proof), MPa		700 to 920

Thermal Properties

Latent Heat of Fusion, J/g		48
Latent Heat of Fusion, J/g		210

Melting Completion (Liquidus), °C		270
Melting Completion (Liquidus), °C		1120

Melting Onset (Solidus), °C		240
Melting Onset (Solidus), °C		950

Specific Heat Capacity, J/kg-K		150
Specific Heat Capacity, J/kg-K		380

Thermal Expansion, µm/m-K		26
Thermal Expansion, µm/m-K		17

Otherwise Unclassified Properties

Base Metal Price, % relative		23
Base Metal Price, % relative		39

Density, g/cm³		10
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		4.4
Embodied Carbon, kg CO₂/kg material		4.6

Embodied Energy, MJ/kg		62
Embodied Energy, MJ/kg		72

Embodied Water, L/kg		880
Embodied Water, L/kg		360

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		12
Resilience: Unit (Modulus of Resilience), kJ/m³		2030 to 3490

Stiffness to Weight: Axial, points		1.4
Stiffness to Weight: Axial, points		7.6

Stiffness to Weight: Bending, points		9.6
Stiffness to Weight: Bending, points		19

Alloy Composition

Aluminum (Al), %		0 to 0.0050
Aluminum (Al), %		0

Antimony (Sb), %		14 to 16
Antimony (Sb), %		0

Arsenic (As), %		0.3 to 0.6
Arsenic (As), %		0

Bismuth (Bi), %		0 to 0.1
Bismuth (Bi), %		0

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Copper (Cu), %		0 to 0.5
Copper (Cu), %		74.1 to 78

Iron (Fe), %		0 to 0.1
Iron (Fe), %		0 to 0.5

Lead (Pb), %		71.9 to 76.4
Lead (Pb), %		0 to 0.020

Magnesium (Mg), %		0
Magnesium (Mg), %		0 to 0.15

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.3

Nickel (Ni), %		0
Nickel (Ni), %		14.5 to 15.5

Niobium (Nb), %		0
Niobium (Nb), %		0 to 0.1

Tin (Sn), %		9.3 to 10.7
Tin (Sn), %		7.5 to 8.5

Zinc (Zn), %		0 to 0.0050
Zinc (Zn), %		0 to 0.5

Residuals, %		0
Residuals, %		0 to 0.3