Grade 704C Zirconium vs. 7049 Aluminum
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while 7049 aluminum belongs to the aluminum alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is 7049 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 | |
| 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 70 |
| Elongation at Break, % | 11 | |
| 6.2 to 7.0 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 36 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 510 to 530 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 420 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 860 |
| Thermal Conductivity, W/m-K | 21 | |
| 130 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 3.1 |
| Embodied Water, L/kg | 460 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 31 to 34 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 1270 to 1440 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 45 |
| Strength to Weight: Axial, points | 20 | |
| 46 to 47 |
| Strength to Weight: Bending, points | 20 | |
| 46 to 47 |
| Thermal Diffusivity, mm2/s | 12 | |
| 51 |
| Thermal Shock Resistance, points | 58 | |
| 22 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 85.7 to 89.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.1 to 0.22 |
| Copper (Cu), % | 0 | |
| 1.2 to 1.9 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0 | |
| 2.0 to 2.9 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.25 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 | |
| 7.2 to 8.2 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |