Grade 704C Zirconium vs. EN 1.4923 Stainless Steel
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while EN 1.4923 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is EN 1.4923 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 190 |
| Elongation at Break, % | 11 | |
| 12 to 21 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 36 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 870 to 980 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 470 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 480 |
| Thermal Conductivity, W/m-K | 21 | |
| 24 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.8 |
| Embodied Water, L/kg | 460 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 570 to 1580 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 31 to 35 |
| Strength to Weight: Bending, points | 20 | |
| 26 to 28 |
| Thermal Diffusivity, mm2/s | 12 | |
| 6.5 |
| Thermal Shock Resistance, points | 58 | |
| 30 to 34 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.18 to 0.24 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 83.5 to 87.1 |
| Manganese (Mn), % | 0 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 0 | |
| 0.3 to 0.8 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |