Grade 704C Zirconium vs. Solder Alloy 117
Both grade 704C zirconium and solder alloy 117 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is solder alloy 117.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 | |
| 11 |
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 23 |
| Elongation at Break, % | 11 | |
| 20 |
| Poisson's Ratio | 0.34 | |
| 0.42 |
| Shear Modulus, GPa | 36 | |
| 8.1 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 33 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 31 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 150 |
| Thermal Conductivity, W/m-K | 21 | |
| 37 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 28 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 11 |
| Embodied Water, L/kg | 460 | |
| 610 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.1 | |
| 1.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 9.0 |
| Strength to Weight: Axial, points | 20 | |
| 0.88 |
| Strength to Weight: Bending, points | 20 | |
| 2.2 |
| Thermal Diffusivity, mm2/s | 12 | |
| 24 |
| Thermal Shock Resistance, points | 58 | |
| 3.7 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 78.4 to 80.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 19.5 to 20.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |