Grade 704C Zirconium vs. SAE-AISI 1039 Steel
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while SAE-AISI 1039 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is SAE-AISI 1039 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 | |
| 180 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 190 |
| Elongation at Break, % | 11 | |
| 14 to 18 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 36 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 610 to 690 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 340 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Conductivity, W/m-K | 21 | |
| 51 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.8 |
| Embodied Water, L/kg | 460 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 88 to 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 310 to 890 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 22 to 24 |
| Strength to Weight: Bending, points | 20 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 58 | |
| 19 to 22 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.37 to 0.44 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 98.5 to 98.9 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |