Grade 704C Zirconium vs. SAE-AISI D3 Steel
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while SAE-AISI D3 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is SAE-AISI D3 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 190 |
| Elongation at Break, % | 11 | |
| 9.8 to 15 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 36 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 770 to 2050 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 480 to 1550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 480 |
| Thermal Conductivity, W/m-K | 21 | |
| 31 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.7 |
| Embodied Water, L/kg | 460 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 97 to 180 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 28 to 74 |
| Strength to Weight: Bending, points | 20 | |
| 24 to 47 |
| Thermal Diffusivity, mm2/s | 12 | |
| 8.3 |
| Thermal Shock Resistance, points | 58 | |
| 23 to 63 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 2.0 to 2.4 |
| Chromium (Cr), % | 0 | |
| 11 to 13.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 80.3 to 87 |
| Manganese (Mn), % | 0 | |
| 0 to 0.6 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0 to 1.0 |
| Vanadium (V), % | 0 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |