Grade 704C Zirconium vs. SAE-AISI D7 Steel

Grade 704C zirconium belongs to the otherwise unclassified metals classification, while SAE-AISI D7 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 704C zirconium and the bottom bar is SAE-AISI D7 steel.

Grade 704C Cast Zirconium SAE-AISI D7 (T30407) Chromium Cold-Work Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		97
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.34
Poisson's Ratio		0.28

Shear Modulus, GPa		36
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		470
Tensile Strength: Ultimate (UTS), MPa		800 to 2120

Thermal Properties

Latent Heat of Fusion, J/g		240
Latent Heat of Fusion, J/g		270

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		480

Thermal Conductivity, W/m-K		21
Thermal Conductivity, W/m-K		27

Thermal Expansion, µm/m-K		5.9
Thermal Expansion, µm/m-K		11

Otherwise Unclassified Properties

Density, g/cm³		6.7
Density, g/cm³		7.6

Embodied Water, L/kg		460
Embodied Water, L/kg		130

Common Calculations

Stiffness to Weight: Axial, points		8.1
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		20
Strength to Weight: Axial, points		29 to 78

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		25 to 48

Thermal Diffusivity, mm²/s		12
Thermal Diffusivity, mm²/s		7.4

Thermal Shock Resistance, points		58
Thermal Shock Resistance, points		27 to 72

Alloy Composition

Carbon (C), %		0 to 0.1
Carbon (C), %		2.2 to 2.5

Chromium (Cr), %		0
Chromium (Cr), %		11.5 to 13.5

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Hafnium (Hf), %		0 to 4.5
Hafnium (Hf), %		0

Hydrogen (H), %		0 to 0.0050
Hydrogen (H), %		0

Iron (Fe), %		0 to 0.3
Iron (Fe), %		76.6 to 81.9

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.6

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.7 to 1.2

Nickel (Ni), %		0
Nickel (Ni), %		0 to 0.3

Nitrogen (N), %		0 to 0.030
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.3
Oxygen (O), %		0

Phosphorus (P), %		0 to 0.010
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0 to 0.6

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Tin (Sn), %		1.0 to 2.0
Tin (Sn), %		0

Vanadium (V), %		0
Vanadium (V), %		3.8 to 4.4

Zirconium (Zr), %		92.9 to 99
Zirconium (Zr), %		0