Grade 704C Zirconium vs. SAE-AISI M46 Steel
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while SAE-AISI M46 steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is SAE-AISI M46 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 36 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 800 to 2300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 450 |
| Thermal Conductivity, W/m-K | 21 | |
| 18 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 8.1 |
| Embodied Water, L/kg | 460 | |
| 150 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 27 to 78 |
| Strength to Weight: Bending, points | 20 | |
| 24 to 48 |
| Thermal Diffusivity, mm2/s | 12 | |
| 4.9 |
| Thermal Shock Resistance, points | 58 | |
| 25 to 71 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 1.2 to 1.3 |
| Chromium (Cr), % | 0 | |
| 3.7 to 4.2 |
| Cobalt (Co), % | 0 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 70 to 73.8 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 8.0 to 8.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.4 to 0.65 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 |
| Tungsten (W), % | 0 | |
| 1.9 to 2.2 |
| Vanadium (V), % | 0 | |
| 3.0 to 3.3 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |