Grade 704C Zirconium vs. C61300 Bronze
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while C61300 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is C61300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 110 |
| Elongation at Break, % | 11 | |
| 34 to 40 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 36 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 550 to 580 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 420 |
| Thermal Conductivity, W/m-K | 21 | |
| 55 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 8.5 |
| Embodied Water, L/kg | 460 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 150 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 230 to 410 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 20 | |
| 18 to 19 |
| Strength to Weight: Bending, points | 20 | |
| 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 15 |
| Thermal Shock Resistance, points | 58 | |
| 19 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 6.0 to 7.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 | |
| 88 to 91.8 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 2.0 to 3.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.15 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0.2 to 0.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |