Grade 704C Zirconium vs. C82500 Copper
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while C82500 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is C82500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 120 |
| Elongation at Break, % | 11 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 36 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 550 to 1100 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 310 to 980 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 390 |
| Thermal Conductivity, W/m-K | 21 | |
| 130 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 8.8 |
| Embodied Water, L/kg | 460 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 11 to 94 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 400 to 4000 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 20 | |
| 18 to 35 |
| Strength to Weight: Bending, points | 20 | |
| 17 to 27 |
| Thermal Diffusivity, mm2/s | 12 | |
| 38 |
| Thermal Shock Resistance, points | 58 | |
| 19 to 38 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 1.9 to 2.3 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.15 to 0.7 |
| Copper (Cu), % | 0 | |
| 95.3 to 97.8 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.35 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.12 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |