Grade 704C Zirconium vs. S35000 Stainless Steel
Grade 704C zirconium belongs to the otherwise unclassified metals classification, while S35000 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is grade 704C zirconium and the bottom bar is S35000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 200 |
| Elongation at Break, % | 11 | |
| 2.3 to 14 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 36 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 1300 to 1570 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 660 to 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Conductivity, W/m-K | 21 | |
| 16 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.8 |
| Embodied Water, L/kg | 460 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 28 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 | |
| 1070 to 3360 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 46 to 56 |
| Strength to Weight: Bending, points | 20 | |
| 34 to 38 |
| Thermal Diffusivity, mm2/s | 12 | |
| 4.4 |
| Thermal Shock Resistance, points | 58 | |
| 42 to 51 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.070 to 0.11 |
| Chromium (Cr), % | 0 | |
| 16 to 17 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 72.7 to 76.9 |
| Manganese (Mn), % | 0 | |
| 0.5 to 1.3 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 3.2 |
| Nickel (Ni), % | 0 | |
| 4.0 to 5.0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0.070 to 0.13 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 1.0 to 2.0 | |
| 0 |
| Zirconium (Zr), % | 92.9 to 99 | |
| 0 |