Grade 705C Zirconium vs. Solder Alloy 161

Both grade 705C zirconium and solder alloy 161 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is grade 705C zirconium and the bottom bar is solder alloy 161.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
38
Elongation at Break, % 13
44
Poisson's Ratio 0.34
0.39
Shear Modulus, GPa 36
14
Tensile Strength: Ultimate (UTS), MPa 540
53

Thermal Properties

Latent Heat of Fusion, J/g 250
48
Specific Heat Capacity, J/kg-K 270
190
Thermal Conductivity, W/m-K 18
49
Thermal Expansion, µm/m-K 5.7
25

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.9
Embodied Water, L/kg 450
910

Common Calculations

Stiffness to Weight: Axial, points 8.1
2.4
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 22
1.7
Strength to Weight: Bending, points 22
3.5
Thermal Diffusivity, mm2/s 9.9
29
Thermal Shock Resistance, points 69
4.1

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.1
0
Copper (Cu), % 0
1.2 to 1.6
Gold (Au), % 0
0 to 0.050
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.3
0 to 0.020
Lead (Pb), % 0
37.3 to 39.3
Nickel (Ni), % 0
0 to 0.010
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.010
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
59.5 to 60.5
Zinc (Zn), % 0
0 to 0.0010
Zirconium (Zr), % 91.9 to 98
0