Grade 705C Zirconium vs. C64200 Bronze
Grade 705C zirconium belongs to the otherwise unclassified metals classification, while C64200 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 705C zirconium and the bottom bar is C64200 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 110 |
| Elongation at Break, % | 13 | |
| 14 to 35 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 36 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 540 to 640 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 230 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 430 |
| Thermal Conductivity, W/m-K | 18 | |
| 45 |
| Thermal Expansion, µm/m-K | 5.7 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 8.3 |
| Embodied Water, L/kg | 450 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 66 | |
| 73 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 790 | |
| 240 to 470 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 22 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 22 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 9.9 | |
| 13 |
| Thermal Shock Resistance, points | 69 | |
| 20 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 6.3 to 7.6 |
| Arsenic (As), % | 0 | |
| 0 to 0.15 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 | |
| 88.2 to 92.2 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Niobium (Nb), % | 2.0 to 3.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 | |
| 1.5 to 2.2 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Zirconium (Zr), % | 91.9 to 98 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |