Grade 8 Babbitt Metal vs. CC751S Brass

Grade 8 Babbitt Metal belongs to the otherwise unclassified metals classification, while CC751S brass belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is grade 8 Babbitt Metal and the bottom bar is CC751S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 15
130
Elastic (Young's, Tensile) Modulus, GPa 24
110
Poisson's Ratio 0.41
0.31
Shear Modulus, GPa 8.5
40
Tensile Strength: Yield (Proof), MPa 23
320

Thermal Properties

Latent Heat of Fusion, J/g 46
190
Melting Completion (Liquidus), °C 270
850
Melting Onset (Solidus), °C 240
810
Specific Heat Capacity, J/kg-K 150
390
Thermal Conductivity, W/m-K 24
110
Thermal Expansion, µm/m-K 24
20

Otherwise Unclassified Properties

Base Metal Price, % relative 19
24
Density, g/cm3 10
8.1
Embodied Carbon, kg CO2/kg material 3.9
2.8
Embodied Energy, MJ/kg 53
46
Embodied Water, L/kg 840
330

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 11
480
Stiffness to Weight: Axial, points 1.3
7.2
Stiffness to Weight: Bending, points 9.2
19
Thermal Diffusivity, mm2/s 16
35

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0 to 0.1
Antimony (Sb), % 14 to 16
0 to 0.5
Arsenic (As), % 0.3 to 0.6
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.050
0
Copper (Cu), % 0 to 0.5
62.7 to 66
Iron (Fe), % 0 to 0.1
0.25 to 0.5
Lead (Pb), % 77.1 to 81.2
0.8 to 2.2
Manganese (Mn), % 0
0 to 0.15
Nickel (Ni), % 0
0 to 0.8
Silicon (Si), % 0
0.65 to 1.1
Tin (Sn), % 4.5 to 5.5
0 to 0.8
Zinc (Zn), % 0 to 0.0050
27.9 to 35.6