Grade C-6 Titanium vs. C78200 Nickel Silver
Grade C-6 titanium belongs to the titanium alloys classification, while C78200 nickel silver belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is grade C-6 titanium and the bottom bar is C78200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 9.0 | |
| 3.0 to 40 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 39 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 890 | |
| 370 to 630 |
| Tensile Strength: Yield (Proof), MPa | 830 | |
| 170 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 160 |
| Melting Completion (Liquidus), °C | 1580 | |
| 1000 |
| Melting Onset (Solidus), °C | 1530 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 390 |
| Thermal Conductivity, W/m-K | 7.8 | |
| 48 |
| Thermal Expansion, µm/m-K | 9.8 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.2 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 28 |
| Density, g/cm3 | 4.5 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 30 | |
| 3.3 |
| Embodied Energy, MJ/kg | 480 | |
| 52 |
| Embodied Water, L/kg | 190 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 | |
| 18 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3300 | |
| 130 to 1440 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 35 | |
| 19 |
| Strength to Weight: Axial, points | 55 | |
| 12 to 21 |
| Strength to Weight: Bending, points | 46 | |
| 14 to 19 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 15 |
| Thermal Shock Resistance, points | 63 | |
| 12 to 21 |
Alloy Composition
| Aluminum (Al), % | 4.0 to 6.0 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 | |
| 63 to 67 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.050 | |
| 7.0 to 9.0 |
| Oxygen (O), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 2.0 to 3.0 | |
| 0 |
| Titanium (Ti), % | 89.7 to 94 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 20.2 to 28.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |